Reinforced High Temperature Superconductors

A time honored way to strengthen materials is internal fiber reinforcement or ¨straw in bricks¨.

But reinforcement is difficult because HTS is made by first melting component powders at ≈ 1200°C, then cooling under oxygen. Reinforcing material placed inside oxidizes at high temperatures, forming impurities which interupt crystal growth and form secondary seeding sites. These weaken HTS crystal strength and hurt performance. HTS strenghtening has so far been limited to external reinforcement such as Packing in Tubes, Deposition on Substrates, or Stainless Steel Encasing.

 

 


A Solution: REINFORCE HTS WITH LONG CONTINUOUS SILICON CARBIDE (SiC) FIBER
̈A simple, reliable and robust reinforcement method for the fabrication of (RE)–Ba–Cu–O bulk superconductors ̈ Devendra K Namburi , Kaiyuan Huang , Wayne Lau, Yunhua Shi, Kysen G Palmer, Anthony R Dennis, David A Cardwell and John H Durrell, 30 March 2020, Superconductor Science and Technology, Volume 33, Number 5 (https://dx.doi.org/10.1088/1361-6668/ab7ec4 (https://iopscience.iop.org/article/10.1088/1361-6668/ab7ec4))
̈A simple, reliable and robust reinforcement method for the fabrication of (RE)–Ba–Cu–O bulk superconductors ̈ Devendra K Namburi , Kaiyuan Huang , Wayne Lau, Yunhua Shi, Kysen G Palmer, Anthony R Dennis, David A Cardwell and John H Durrell, 30 March 2020, Superconductor Science and Technology, Volume 33, Number 5 (https://dx.doi.org/10.1088/1361-6668/ab7ec4 (https://iopscience.iop.org/article/10.1088/1361-6668/ab7ec4))

Open Article

RESULT: 40% gain in strengh with just three 100 μm thick SiC fibers in a 25mm diameter sample.

Silicon in SiC fibers reacts at high temperatures with O2 creating a layer of inert SiO2 preventing further oxidation. This is similar to how chromium (Cr) makes steel stainless.